Technical Data Sheet
Chronifer Labor 13% is a free cutting chromium stainless steel with 13 % Cr which is manufactured in Rod, Bar and coil. Chronifer Labor 13% is resists to water and stream corrosion after tempering and a forced polishing of the parts. For optimum corrosion resistance, surfaces must be free of scale and foreign particles and finished parts should be passivated. Condition T is pre-tempered to 26-32 HRC. (AISI 416 Stainless Steel, WS 1.4005)
| Chemical Composition Limits | |||||||
| Weight % | C | Si | Mn | P | S | Cr | Fe |
| CHRONIFER LABOR 13% | 0.15 max | 1.00 max | 1.50 max | 0.06 max | 0.15-0.35 | 12.00-14.00 | Rem |
| Other Chemically similar Specifications | |||||||
| Weight % | C | Si | Mn | P | S | Cr | Fe |
| WS 1.4005 | 0.15 max | 1.00 max | 1.50 max | 0.06 max | 0.15-0.35 | 12.00-14.00 | Rem |
| DIN X 12 CrS 13 | 0.15 max | 1.00 max | 1.50 max | 0.06 max | 0.15-0.35 | 12.00-14.00 | Rem |
| AISI 416 | 0.15 max | 1.00 max | 1.50 max | 0.06 max | 0.15-0.35 | 12.00-14.00 | Rem |
| AFNOR Z11 C13 | 0.15 max | 1.00 max | 1.50 max | 0.06 max | 0.15-0.35 | 12.00-14.00 | Rem |
Diameters
Ø< 2.00 mm: cold drawn and polished
Ø>= 2.00mm: cold drawn, ground and polished. Surface roughness N6-N7
Availability
In rods, bars, standard length 3m (2m) and in coil
Tolerances
h8 more accurate tolerances on request
Mechanical properties
Tensile strength at delivery form 650-850 N/mm 2
After annealing 500-700 N/mm 2
Heat Treatment
Hardening in oil 950 to 1000 ºC, content of carbon must be above 0.9%
tempering 600-700 ºC
Maximum hardness
43 HRC
Cutting rate
40 to 65 m/mm depending on the lubrication oil, the cutting tool, the shape of parts etc.
Standard Stock
most current dimensions from 0.80 to 13m round (English sizes 1/4", 1/8")